Submerged Entry Nozzle for Continuous Casting

Protect the molten steel from oxidation when it flows into the crystallizer from the tundish, evenly distribute the molten steel into the crystallizer, and control the flow state of the molten steel in the crystallizer, with good slag resistance, anti-blocking, عمر خدمة طويل, and low accident rate.

Submerged nozzle physical and chemical indicators

المؤشرات الفيزيائية والكيميائية：

غرض	فِهرِس
	JSK55	JSK50	JSK45	JSK40
ال2ا3  %	≥55	≥50	≥45	≥40
ج %	≥16	≥18	≥20	≥22
Flexural Strength MPa	≥5.5	≥5.5	≥5.5	≥5
المسامية الظاهرة٪	≥19	≥19	≥19	≥19
الكثافة الظاهرية جم / سم3	≥2.36	≥2.32	≥2.28	≥2.18

Slag Area：

غرض	فِهرِس
	Z75	Z70	Z65	Z55
ZrO2  %	≥75	≥70	≥65	≥55
ج %	≥9	≥12	≥15	≥18
Apparent porosity %	≥21	≥21	≥21	≤22
الكثافة الظاهرية جم / سم3	≥3.6	≥3.5	≥3.4	≥3.2

Introduction to the production process of the submerged entry nozzle

The production process of submerged nozzles requires various raw materials to be mixed into a uniform composite powder, which is then isostatically pressed into the desired shape of the green body. This is then sintered at high temperature to form a product with a certain strength, which is then shaped and processed into the required size. Finally, after inspection, it is packaged and shipped out.

Structure type of submerged entry nozzles (SEN)

Submerged entry nozzles can be broadly categorized by their appearance and internal structure, as shown in the figure below.

Type A is a submerged nozzle with two or four side holes; Type B is a straight-through submerged nozzle; Type C is a submerged nozzle with a hemispherical bowl-shaped mouth, a combined nozzle used in conjunction with a tundish nozzle; Type D is a thin-walled, irregular-shaped submerged nozzle, typically used for thin slab continuous casting; Type E has a flat end face, typically a quick-change nozzle; Type F has a zirconium core embedded within it, used for billet continuous casting.

What conditions does the submerged nozzle need to meet?

1) Ensure the flow rate of molten steel at normal pulling speed.
(2) Make the heat flow distribution in the mold and the cross section of the ingot as uniform as possible;
(3) Facilitate the rapid melting of protective slag;
(4) Facilitate the floating of inclusions without slag rolling;
(5) Avoid violent turbulence of the steel liquid level in the crystallizer;
(6) Easy to install.

Selection of immersed nozzle material

In the early stage of continuous casting, the fused quartz immersion nozzle with good thermal stability and high purity can meet the casting of ordinary carbon steel, low manganese steel, aluminum killed steel and other steel types. لكن, it is severely corroded under the conditions of high manganese steel and high alkalinity slag. At this time, the aluminum carbon immersion nozzle is widely used. The raw materials of aluminum carbon immersion nozzle are special grade bauxite, fused corundum or sintered corundum, إلخ., with the addition of graphite and antioxidants. The product has the advantages of corrosion resistance and thermal shock resistance.